| AFCIMOL Range are high solids thixotropic refractory dressings
with in built excellent suspension characteristics & anti-settling
properties specially recommended for exceptionally smooth casting surface
finish & dimensional accuracy for ferrous & Non ferrous foundries. |
| |
AFCIMOL is available in range of special refractory dressings
base such as Graphite, Graphite-Zircon, Zircon, Zircon-Graphite, Magnesite,
Ceramic etc to suit individual application characteristics.
|
| |
| PHYSICAL
STATE |
- AFCIMOL
is available in POWDER, PASTE & READY FOR USE FORM (for Dipping).
|
| |
| CODE |
PRODUCT |
THINNER |
FILLER |
CHARACTERISTICS |
APPLICATION |
| F011 |
AFCIMOL
11 |
SOLVENT |
GRAPHITE |
DILUTION RATIO FOR PASTE:
1 : 1.5 VISCOSITY ON DILUTION : 10-16 sec SPECIFIC GRAVITY ON DILUTION
: 0.9 TO 1.0
BAUME : 0 TO 20SETTLING PERCENTAGE / HR : 25 TO 35 %
|
CAST
IRON, S.G. IRON, NI -HARD, MALLEABLEOIL/ SHELL/ HOT /COLD BOX/SILICATE
CORES/ MOULD |
| F021 |
AFCIMOL
21 |
IPA |
| F031 |
AFCIMOL
31 |
AIR
DRYING |
| F041 |
AFCIMOL
41 |
SOLVENT
|
GRAPHITE-ZIRCON |
DILUTION RATIO FOR PASTE:
1 : 2 VISCOSITY ON DILUTION : 12-16 sec SPECIFIC GRAVITY ON DILUTION
: 1.0 TO 1.2BAUME : 0 TO 20SETTLING PERCENTAGE / HR : 25 TO 35 %
|
CAST
IRON, S.G. IRON, HEAVY GREY IRONOIL/ CO2/ SHELL/ HOT /COLD BOX /SILICATE
CORES/ MOULD |
| F051 |
AFCIMOL
51 |
IPA |
| F061 |
AFCIMOL
61 |
AIR
DRYING |
| F071 |
AFCIMOL
71 |
SOLVENT |
ZIRCON |
DILUTION RATIO FOR PASTE:
1 : 0.5 VISCOSITY ON DILUTION : 12-16 sec SPECIFIC GRAVITY ON DILUTION
: 1.4 TO 1.6BAUME : 44 TO 65SETTLING PERCENTAGE / HR : 10 TO 20
% |
ALLOY
IRON, ALLOY STEEL, CARBON STEEL, STAINLESS STEEL, S.G. IRON,&
HEAVY GREY IRON CASTINGS OIL/ SHELL/ HOT /COLD BOX/SILICATE CORES/
MOULD |
| F081 |
AFCIMOL
81 |
IPA |
| F091 |
AFCIMOL
91 |
AIR
DRYING |
| F0101 |
AFCIMOL
101 |
SOLVENT
|
ZIRCON-GRAPHITE |
DILUTION RATIO FOR PASTE:
1 : 1.5 VISCOSITY ON DILUTION : 12-16 sec SPECIFIC GRAVITY ON DILUTION
: 1.2 TO 1.4BAUME : 25 TO 40SETTLING PERCENTAGE / HR : 10 TO 20
% |
STEEL,
S.G. IRON, HEAVY GREY IRONOIL/ CO2/ SHELL/ HOT/ COLD BOX /SILICATE
CORES/ MOULD |
| F0111 |
AFCIMOL
111 |
IPA |
| F0121 |
AFCIMOL
121 |
AIR
DRYING |
| F0131 |
AFCIMOL
131 |
SOLVENT
|
MAGNESITE |
DILUTION RATIO FOR PASTE:
1 : 1 VISCOSITY ON DILUTION : 12-16 sec SPECIFIC GRAVITY ON DILUTION
: 1.2 TO 1.4BAUME : 25 TO 40SETTLING PERCENTAGE / HR : 10 TO 20
% |
MANGANESE/, STEEL, HEAVY GREY IRON CASTINGSOIL/ SHELL/ HOT
/ COLD BOX /SILICATE CORES/ MOULD |
| F0141 |
AFCIMOL
141 |
| IPA |
| F0151 |
AFCIMOL
151 |
AIR
DRYING |
| F0161 |
AFCIMOL
161 |
SOLVENT |
CERAMIC |
DILUTION RATIO FOR PASTE:
1 : 1 VISCOSITY ON DILUTION : 15-25 sec SPECIFIC GRAVITY ON DILUTION
: 1.3 TO 1.5BAUME : 30 TO 45SETTLING PERCENTAGE / HR : 10 TO 20
% |
NON-FERROUS CASTINGS LIKE ZINC, BRONZE, BRASS; ALUMINIUM, AND
MILD STEELOIL/ CO2/ SHELL/ HOT/ COLD BOX/SILICATE CORES/ MOULD |
| F0171 |
AFCIMOL
17 1 |
IPA |
| F0181 |
AFCIMOL
181 |
AIR
DRYING |
| F0191 |
AFCIMOL
191 |
SOLVENT
|
THINNER |
SPECIFIC GRAVITY : 0.7 TO 0.8 |
SOLVENT/ ISOPROPYL ALCOHOL / TOLUENE BASED THINNER WITH OR
WITHOUT BINDER FOR DILUTION OF SPIRIT BASED CORE & MOULD WASHES |
| F0201 |
AFCIMOL
201 |
IPA |
| F0211 |
AFCIMOL
211 |
AIR
DRYING |
|
| |
|
|
| |
| APPLICATION FEATURES |
- Due to excellent
fluidity characteristics coating can be achieved by dilution to specified
viscosity/ baume as per individual application needs ,
- Direct application
by dipping for Ready For Use form after proper mixing.
- In case of powder,
dilute the powder with Solvent or Spirit, first mixing well to obtain
a paste form and then diluting to required viscosity. Recommended
dilution ratio is given in the above table with respect to individual
refractory dressings.
- Torching or oven
baking after air drying for 15 to 20 minutes, for best results of
all coats.
- Applications, by
brushing, swabbing, or spraying may be used as per required consistency
of coating.
|
| |
NOTE
:
- Dilution Ratio of AFCIMOL RANGE mentioned in the above table is
for application by Dipping to obtain
- Ready For Use form, which may vary according to foundry suitability.
- AFCIMOL RANGE is a highly inflammable range containing Alcohol.
Hence keep away from high heat / flames.
- Also keep the container tightly closed after use to avoid atmospheric
exposure.
|
| |
| PRODUCT
FEATURES : |
- Highly Refractoriness
with optimum penetration properties,
- High solids thixotropic
dressings with in built anti-settling properties ,
- In built Anti-fungus
& Anti-settling properties.
- Batch consistency
hence consistent quality coatings leading to superior surface finish.
- Superb suspension
characteristics hence good mixability,
- Higher shelf life
of cores & moulds due to anti-hydrating property,
- Low gas evolution
during pouring,
- Excellent adherence
to the mould/ core due to superb consistency & homogenous nature,
- Excellent Coverage,
uniform coating characteristics ,
- Smooth Casting
surface finish & Dimensional accuracy,
- Economical due
to reduced fettling and cleaning costs.
Our wide range of products
include:
*Core & Mould Binders *Sand
Additives *Resin Coated Sand *Parting Agent *Water/ Solvent
Based Refractory Coatings *Exothermic and Insulating
Compound/ Sleeves *Treatment Fluxes *
Bentonite * Slag Holding Compound *Carbon
Pick-up |
| |
| STANDARD
PACKING |
- Available in 50KGS.
BAGS For POWDER & PASTE.
- Available in 35/
50 KGS. CARBOUYS For READY FOR USE.
|
| |